TARDIGRADE

ECAS 290

TWO COMPONENT, SOLVENT FREE, EPOXY BASED, SELF LEVELING ANTISTATIC TOP COATING

Tardigrade ECAS 290 is a solvent free, two component, self leveling and antistatic epoxy based coating material.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • On automotive, pharmaceuticals, chemistry, electrical, electronics and similar markets manufacturing and storage areas
  • In plane hangars and warehouses where flammable and explosive materials are stored
  • In electrical equipment manufacturing facilities, server rooms, automation rooms, factories, surgery rooms and printing houses

    It is used as the main coating material for floors where antistatic coating systems are required.

ADVANTAGES

  • Antistatic properties
  • Highly resistant to mechanical loads and chemicals
  • Solvent free
  • Conductive
  • Excellent penetration and adhesion ability
  • It provides a hygienic environment by preventing the formation of germs and bacteria
  • Easy application
  • Liquid proof
  • Semi-gloss surface.

TARDIGRADE

ECAS 290

TWO COMPONENT, SOLVENT FREE, EPOXY BASED, SELF LEVELING ANTISTATIC TOP COATING

Tardigrade ECAS 290 is a solvent free, two component, self leveling and antistatic epoxy based coating material.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • On automotive, pharmaceuticals, chemistry, electrical, electronics and similar markets manufacturing and storage areas
  • In plane hangars and warehouses where flammable and explosive materials are stored
  • In electrical equipment manufacturing facilities, server rooms, automation rooms, factories, surgery rooms and printing houses

    It is used as the main coating material for floors where antistatic coating systems are required.

ADVANTAGES

  • Antistatic properties
  • Highly resistant to mechanical loads and chemicals
  • Solvent free
  • Conductive
  • Excellent penetration and adhesion ability
  • It provides a hygienic environment by preventing the formation of germs and bacteria
  • Easy application
  • Liquid proof
  • Semi-gloss surface.

TARDIGRADE

ECAS 290

TWO COMPONENT, SOLVENT FREE, EPOXY BASED, SELF LEVELING ANTISTATIC TOP COATING

Tardigrade ECAS 290 is a solvent free, two component, self leveling and antistatic epoxy based coating material.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • On automotive, pharmaceuticals, chemistry, electrical, electronics and similar markets manufacturing and storage areas
  • In plane hangars and warehouses where flammable and explosive materials are stored
  • In electrical equipment manufacturing facilities, server rooms, automation rooms, factories, surgery rooms and printing houses

    It is used as the main coating material for floors where antistatic coating systems are required.

ADVANTAGES

  • Antistatic properties
  • Highly resistant to mechanical loads and chemicals
  • Solvent free
  • Conductive
  • Excellent penetration and adhesion ability
  • It provides a hygienic environment by preventing the formation of germs and bacteria
  • Easy application
  • Liquid proof
  • Semi-gloss surface.

APPEARANCE

Mix (Part A +Part B): Ral Colors suitable for anti-static

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 20 kg. net – Part B: 5 kg. net
  • Total Set: 25 kg. net – Total Set: 27,55 kg. gross
  • Part A: 4 kg. net – Part B: 1 kg. net
  • Total Set: 5 kg. net – Total Set: 5,90 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

APPEARANCE

Mix (Part A +Part B): Ral Colors suitable for anti-static

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 20 kg. net – Part B: 5 kg. net
  • Total Set: 25 kg. net – Total Set: 27,55 kg. gross
  • Part A: 4 kg. net – Part B: 1 kg. net
  • Total Set: 5 kg. net – Total Set: 5,90 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

APPEARANCE

Mix (Part A +Part B): Ral Colors suitable for anti-static

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 20 kg. net – Part B: 5 kg. net
  • Total Set: 25 kg. net – Total Set: 27,55 kg. gross
  • Part A: 4 kg. net – Part B: 1 kg. net
  • Total Set: 5 kg. net – Total Set: 5,90 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,35 kg/litre (± %3)

Viscosity

Mixed Resin: 1.000-2.000 mPa.s

Shore D Hardness

7 days: 75-85 (ASTM D2240-05)

Compressive Strength

28 days: > 90 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 40 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 25 mg (CS 10/1000/1000)

(ASTM D4060-14)

Electrostatic Behavior

104 ≤ Rg ≤ 106 Ω (IEC 61340-4-1)

Duration of Use After Mixing

40 – 60 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,35 kg/litre (± %3)

Viscosity

Mixed Resin: 1.000-2.000 mPa.s

Shore D Hardness

7 days: 75-85 (ASTM D2240-05)

Compressive Strength

28 days: > 90 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 40 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 25 mg (CS 10/1000/1000)

(ASTM D4060-14)

Electrostatic Behavior

104 ≤ Rg ≤ 106 Ω (IEC 61340-4-1)

Duration of Use After Mixing

40 – 60 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,35 kg/litre (± %3)

Viscosity

Mixed Resin: 1.000-2.000 mPa.s

Shore D Hardness

7 days: 75-85 (ASTM D2240-05)

Compressive Strength

28 days: > 90 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 40 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 25 mg (CS 10/1000/1000)

(ASTM D4060-14)

Electrostatic Behavior

104 ≤ Rg ≤ 106 Ω (IEC 61340-4-1)

Duration of Use After Mixing

40 – 60 minutes

Total Curing Time

7 days