TARDIGRADE

ECTX 250

TWO COMPONENT, SOLVENT FREE, EPOXY BASED THIXOTROPIC TOP COATING MATERIAL

Tardigrade ECTX 250, is a high viscosity, solvent free, two component, colored, orange peel textured, epoxy based top coat floor coating.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • Warehousing and assembly areas
  • Production areas, factories and workshops
  • Normal up to medium heavy wear e.g. storage and assembly halls, maintenance workshops garages, loading ramps, airplane hangars
  • Wet process areas in laboratories, food, chemistry and pharmaceutical industries
  • Control rooms, thermal and hydroelectric power plants

    used as textured floor coating

ADVANTAGES

  • Due to its high thixotropic feature it provides a textured and non-slip surface
  • High bond strength
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Fillable
  • Liquid proof
  • Hygienic and easy to clean
  • Semi elastic
  • Resistant to mechanical loads, abrasion and chemicals

TARDIGRADE

ECTX 250

TWO COMPONENT, SOLVENT FREE, EPOXY BASED THIXOTROPIC TOP COATING MATERIAL

Tardigrade ECTX 250, is a high viscosity, solvent free, two component, colored, orange peel textured, epoxy based top coat floor coating.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • Warehousing and assembly areas
  • Production areas, factories and workshops
  • Normal up to medium heavy wear e.g. storage and assembly halls, maintenance workshops garages, loading ramps, airplane hangars
  • Wet process areas in laboratories, food, chemistry and pharmaceutical industries
  • Control rooms, thermal and hydroelectric power plants

    used as textured floor coating

ADVANTAGES

  • Due to its high thixotropic feature it provides a textured and non-slip surface
  • High bond strength
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Fillable
  • Liquid proof
  • Hygienic and easy to clean
  • Semi elastic
  • Resistant to mechanical loads, abrasion and chemicals

TARDIGRADE

ECTX 250

TWO COMPONENT, SOLVENT FREE, EPOXY BASED THIXOTROPIC TOP COATING MATERIAL

Tardigrade ECTX 250, is a high viscosity, solvent free, two component, colored, orange peel textured, epoxy based top coat floor coating.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • Warehousing and assembly areas
  • Production areas, factories and workshops
  • Normal up to medium heavy wear e.g. storage and assembly halls, maintenance workshops garages, loading ramps, airplane hangars
  • Wet process areas in laboratories, food, chemistry and pharmaceutical industries
  • Control rooms, thermal and hydroelectric power plants

    used as textured floor coating

ADVANTAGES

  • Due to its high thixotropic feature it provides a textured and non-slip surface
  • High bond strength
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Fillable
  • Liquid proof
  • Hygienic and easy to clean
  • Semi elastic
  • Resistant to mechanical loads, abrasion and chemicals

APPEARANCE

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 25,20kg. net – Part B: 4,80 kg. net
  • Total Set: 30 kg. net – Total Set: 32,55 kg. gross
  • Part A: 5,04 kg. net – Part B: 0,96 kg. net
  • Total Set: 6 kg. net – Total Set: 6,90 kg. gross

*Barrels are available if requested.

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

APPEARANCE

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 25,20kg. net – Part B: 4,80 kg. net
  • Total Set: 30 kg. net – Total Set: 32,55 kg. gross
  • Part A: 5,04 kg. net – Part B: 0,96 kg. net
  • Total Set: 6 kg. net – Total Set: 6,90 kg. gross

*Barrels are available if requested.

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

APPEARANCE

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 25,20kg. net – Part B: 4,80 kg. net
  • Total Set: 30 kg. net – Total Set: 32,55 kg. gross
  • Part A: 5,04 kg. net – Part B: 0,96 kg. net
  • Total Set: 6 kg. net – Total Set: 6,90 kg. gross

*Barrels are available if requested.

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,55 kg/litre (± %3)

Viscosity

Mixed Resin: 5.000 – 10.000 mPa.s

Shore D Hardness

7 days: 75 – 85 (ASTM D2240-05)

Compressive Strength

28 days: > 90 N/mm² (ASTM D695-10)

Flexural Strength

7 days : > 35 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 50 mg (CS 10/1000/1000)

(ASTM D4060-14)

Duration of Use After Mixing

40 – 60 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,55 kg/litre (± %3)

Viscosity

Mixed Resin: 5.000 – 10.000 mPa.s

Shore D Hardness

7 days: 75 – 85 (ASTM D2240-05)

Compressive Strength

28 days: > 90 N/mm² (ASTM D695-10)

Flexural Strength

7 days : > 35 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 50 mg (CS 10/1000/1000)

(ASTM D4060-14)

Duration of Use After Mixing

40 – 60 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,55 kg/litre (± %3)

Viscosity

Mixed Resin: 5.000 – 10.000 mPa.s

Shore D Hardness

7 days: 75 – 85 (ASTM D2240-05)

Compressive Strength

28 days: > 90 N/mm² (ASTM D695-10)

Flexural Strength

7 days : > 35 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 50 mg (CS 10/1000/1000)

(ASTM D4060-14)

Duration of Use After Mixing

40 – 60 minutes

Total Curing Time

7 days