TARDIGRADE

PCSL 210

TWO COMPONENT, SOLVENT FREE, POLYURETHANE BASED SELF LEVELING COATING MATERIAL

Tardigrade PCSL 210 is a low viscosity, solvent free, two component, self leveling, multi-purpose polyurethane based coating material.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • Wet process areas in laboratories, food, chemistry and pharmaceutical industries
  • Exhibition halls, museums and offices
  • Warehousing and assembly areas
  • In exhibition halls, museums and office areas
  • Roof, terrace, ponds and underground water storage applications

ADVANTAGES

  • Low viscosity
  • Ultrahigh bond strength
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Covers static cracks
  • Gloss finish
  • Liquid proof
  • Hygienic and easy to clean
  • Resistant to mechanical loads, abrasion and chemicals

TARDIGRADE

PCSL 210

TWO COMPONENT, SOLVENT FREE, POLYURETHANE BASED SELF LEVELING COATING MATERIAL

Tardigrade PCSL 210 is a low viscosity, solvent free, two component, self leveling, multi-purpose polyurethane based coating material.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • Wet process areas in laboratories, food, chemistry and pharmaceutical industries
  • Exhibition halls, museums and offices
  • Warehousing and assembly areas
  • In exhibition halls, museums and office areas
  • Roof, terrace, ponds and underground water storage applications

ADVANTAGES

  • Low viscosity
  • Ultrahigh bond strength
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Covers static cracks
  • Gloss finish
  • Liquid proof
  • Hygienic and easy to clean
  • Resistant to mechanical loads, abrasion and chemicals

TARDIGRADE

PCSL 210

TWO COMPONENT, SOLVENT FREE, POLYURETHANE BASED SELF LEVELING COATING MATERIAL

Tardigrade PCSL 210 is a low viscosity, solvent free, two component, self leveling, multi-purpose polyurethane based coating material.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • Wet process areas in laboratories, food, chemistry and pharmaceutical industries
  • Exhibition halls, museums and offices
  • Warehousing and assembly areas
  • In exhibition halls, museums and office areas
  • Roof, terrace, ponds and underground water storage applications

ADVANTAGES

  • Low viscosity
  • Ultrahigh bond strength
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Covers static cracks
  • Gloss finish
  • Liquid proof
  • Hygienic and easy to clean
  • Resistant to mechanical loads, abrasion and chemicals

APPEARANCE

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 18 kg. net – Part B: 6 kg. net – Part B: 6 kg.

  • Total Set: 24 kg. net – Total Set: 26,55 kg. gross

  • Part A: 3,75 kg. net – Part B: 1,25 kg. net

  • Total Set: 5 kg. net – Total Set: 5,90 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Polyurethane Resin Part B: Polyurethane Hardener

APPEARANCE

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 18 kg. net – Part B: 6 kg. net

  • Total Set: 24 kg. net – Total Set: 26,55 kg. gross

  • Part A: 3,75 kg. net – Part B: 1,25 kg. net

  • Total Set: 5 kg. net – Total Set: 5,90 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Polyurethane Resin Part B: Polyurethane Hardener

APPEARANCE

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 18 kg. net – Part B: 6 kg. net

  • Total Set: 24 kg. net – Total Set: 26,55 kg. gross

  • Part A: 3,75 kg. net – Part B: 1,25 kg. net

  • Total Set: 5 kg. net – Total Set: 5,90 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Polyurethane Resin Part B: Polyurethane Hardener

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,25 kg/litre(± %3)

Viscosity

Mixed Resin: 1.000-2.000 mPa.s

Shore A Hardness

7 days: 80-90 (ASTM D2240-05)

Bond Strength

7 days : > 2,5 N/mm² (Beton) (ASTM D7234)

Abrasion Strength

7 days: < 30 mg (CS 10/1000/1000)

(ASTM D4060-14)

Elongation at Break

7 days : > %100 (ASTM D638)

Duration of Use After Mixing

30 – 50 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,25 kg/litre

(± %3)

Viscosity

Mixed Resin: 1.000-2.000 mPa.s

Shore A Hardness

7 days: 80-90 (ASTM D2240-05)

Bond Strength

7 days : > 2,5 N/mm² (Beton) (ASTM D7234)

Abrasion Strength

7 days: < 30 mg (CS 10/1000/1000)

(ASTM D4060-14)

Elongation at Break

7 days : > %100 (ASTM D638)

Duration of Use After Mixing

30 – 50 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,25 kg/litre (± %3)

Viscosity

Mixed Resin: 1.000-2.000 mPa.s

Shore A Hardness

7 days: 80-90 (ASTM D2240-05)

Bond Strength

7 days : > 2,5 N/mm² (Beton) (ASTM D7234)

Abrasion Strength

7 days: < 30 mg (CS 10/1000/1000)

(ASTM D4060-14)

Elongation at Break

7 days : > %100 (ASTM D638)

Duration of Use After Mixing

30 – 50 minutes

Total Curing Time

7 days