PCTX 250

TWO COMPONENT, SOLVENT FREE, THIXOTROPIC POLYURETHANE BASED TOP COAT

Tardigrade PCTX 250 is a high viscosity, solvent free, two component, orange peel textured, polyurethane based coating material.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • Warehousing and assembly areas
  • Production areas, factories and workshops
  • Normal up to medium heavy wear e.g. storage and assembly halls, maintenance workshops garages, loading ramps, airplane hangars
  • Wet process areas in laboratories, food, chemistry and pharmaceutical industries
  • Roof, terrace, ponds and underground water storage applications

    It is used as a main coating and waterproofing material.

ADVANTAGES

  • Due to its high thixotropic feature it provides a textured and non-slip surface
  • High bond strength
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Covers static cracks
  • Liquid proof
  • Hygienic and easy to clean
  • Semi elastic
  • Resistant to mechanical loads, abrasion and chemicals

TARDIGRADE

PCTX 250

TWO COMPONENT, SOLVENT FREE, THIXOTROPIC POLYURETHANE BASED TOP COAT

Tardigrade PCTX 250 is a high viscosity, solvent free, two component, orange peel textured, polyurethane based coating material.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • Warehousing and assembly areas
  • Production areas, factories and workshops
  • Normal up to medium heavy wear e.g. storage and assembly halls, maintenance workshops garages, loading ramps, airplane hangars
  • Wet process areas in laboratories, food, chemistry and pharmaceutical industries
  • Roof, terrace, ponds and underground water storage applications

    It is used as a main coating and waterproofing material.

ADVANTAGES

  • Due to its high thixotropic feature it provides a textured and non-slip surface
  • High bond strength
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Covers static cracks
  • Liquid proof
  • Hygienic and easy to clean
  • Semi elastic
  • Resistant to mechanical loads, abrasion and chemicals

TARDIGRADE

PCTX 250

TWO COMPONENT, SOLVENT FREE, THIXOTROPIC POLYURETHANE BASED TOP COAT

Tardigrade PCTX 250 is a high viscosity, solvent free, two component, orange peel textured, polyurethane based coating material.

FIELDS OF APPLICATION

  • On concrete and cement based mineral surfaces
  • Warehousing and assembly areas
  • Production areas, factories and workshops
  • Normal up to medium heavy wear e.g. storage and assembly halls, maintenance workshops garages, loading ramps, airplane hangars
  • Wet process areas in laboratories, food, chemistry and pharmaceutical industries
  • Roof, terrace, ponds and underground water storage applications

    It is used as a main coating and waterproofing material.

ADVANTAGES

  • Due to its high thixotropic feature it provides a textured and non-slip surface
  • High bond strength
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Covers static cracks
  • Liquid proof
  • Hygienic and easy to clean
  • Semi elastic
  • Resistant to mechanical loads, abrasion and chemicals

APPEARANCE

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 25,50 kg. net – Part B: 4,50 kg. net

  • Total Set: 30 kg. net – Total Set: 32,55 kg. gross

  • Part A : 5,10 kg. net – Part B: 0,90 kg. net

  • Total Set: 6 kg. net – Total Set: 6,90 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Polyurethane Resin Part B: Polyurethane Hardener

APPEARANCE

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 25,50 kg. net – Part B: 4,50 kg. net

  • Total Set: 30 kg. net – Total Set: 32,55 kg. gross

  • Part A : 5,10 kg. net – Part B: 0,90 kg. net

  • Total Set: 6 kg. net – Total Set: 6,90 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Polyurethane Resin Part B: Polyurethane Hardener

APPEARANCE

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating. This does not affect the physical and chemical resistance of coating.

PACKAGING

  • Part A: 25,50 kg. net – Part B: 4,50 kg. net

  • Total Set: 30 kg. net – Total Set: 32,55 kg. gross

  • Part A : 5,10 kg. net – Part B: 0,90 kg. net

  • Total Set: 6 kg. net – Total Set: 6,90 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Polyurethane Resin Part B: Polyurethane Hardener

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,40 kg/liter (± %3)

Viscosity

Mixed Resin: 5.000 – 10.000 mPa.s

Shore A Hardness

7 days: 85 – 95 (ASTM D2240-05)

Bond Strength

7 days : > 2,5 N/mm² (Beton) (ASTM D7234)

Abrasion Strength

7 days: < 60 mg (CS 10/1000/1000) (ASTM D4060-14)

Elongation at Break

7 days: > %70 (ASTM D638)

Duration of Use After Mixing

40 – 60 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,50 kg/litre (± %3)

Density

Mixed Resin: 1,40 kg/liter (± %3)

Viscosity

Mixed Resin: 5.000 – 10.000 mPa.s

Shore A Hardness

7 days: 85 – 95 (ASTM D2240-05)

Bond Strength

7 days : > 2,5 N/mm² (Beton) (ASTM D7234)

Abrasion Strength

7 days: < 60 mg (CS 10/1000/1000) (ASTM D4060-14)

Elongation at Break

7 days: > %70 (ASTM D638)

Duration of Use After Mixing

40 – 60 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,40 kg/liter (± %3)

Viscosity

Mixed Resin: 5.000 – 10.000 mPa.s

Shore A Hardness

7 days: 85 – 95 (ASTM D2240-05)

Bond Strength

7 days : > 2,5 N/mm² (Beton) (ASTM D7234)

Abrasion Strength

7 days: < 60 mg (CS 10/1000/1000) (ASTM D4060-14)

Elongation at Break

7 days: > %70 (ASTM D638)

Duration of Use After Mixing

40 – 60 minutes

Total Curing Time

7 days