TARDIGRADE

EPMT 140

TWO COMPONENT, SOLVENT FREE, MOISTURE TOLERANT, EPOXY RESIN BASED PRIMER

Tardigrade EPMT 140, is a low viscosity, solvent free two-part epoxy resin based primer with high adhesion capability to moist concrete and mineral substrates.

FIELDS OF APPLICATION

  • Internal and external substrates
  • On concrete and cement based mineral surfaces
  • Specifically for moisture surfaces
  • Primer for all Tardigrade epoxy or polyurethane based systems
  • Binder for epoxy based leveling mortars and mortar screeds
  • Surfaces that require cast and the repair mortar as it is used as filler with aggregate

ADVANTAGES

  • Low viscosity
  • High bond strength on moist surfaces
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Suitable for interior and exterior areas
  • High chemical resistance

TARDIGRADE

EPMT 140

TWO COMPONENT, SOLVENT FREE, MOISTURE TOLERANT, EPOXY RESIN BASED PRIMER

Tardigrade EPMT 140, is a low viscosity, solvent free two-part epoxy resin based primer with high adhesion capability to moist concrete and mineral substrates.

FIELDS OF APPLICATION

  • Internal and external substrates
  • On concrete and cement based mineral surfaces
  • Specifically for moisture surfaces
  • Primer for all Tardigrade epoxy or polyurethane based systems
  • Binder for epoxy based leveling mortars and mortar screeds
  • Surfaces that require cast and the repair mortar as it is used as filler with aggregate

ADVANTAGES

  • Low viscosity
  • High bond strength on moist surfaces
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Suitable for interior and exterior areas
  • High chemical resistance

TARDIGRADE

EPMT 140

TWO COMPONENT, SOLVENT FREE, MOISTURE TOLERANT, EPOXY RESIN BASED PRIMER

Tardigrade EPMT 140, is a low viscosity, solvent free two-part epoxy resin based primer with high adhesion capability to moist concrete and mineral substrates.

FIELDS OF APPLICATION

  • Internal and external substrates
  • On concrete and cement based mineral surfaces
  • Specifically for moisture surfaces
  • Primer for all Tardigrade epoxy or polyurethane based systems
  • Binder for epoxy based leveling mortars and mortar screeds
  • Surfaces that require cast and the repair mortar as it is used as filler with aggregate

ADVANTAGES

  • Low viscosity
  • High bond strength on moist surfaces
  • Solvent free
  • Ultrahigh penetrating ability
  • Easy application
  • Suitable for interior and exterior areas
  • High chemical resistance

APPEARANCE

Part A (Epoxy Resin): Liquid – Transparent

Part B (Epoxy Hardener): Liquid – Pale Yellow

PACKAGING

  • Part A: 12 kg. net – Part B: 8 kg. net

  • Total Set: 20 kg. net – Total Set : 22,55 kg. gross

  • Part A: 1,8 kg. net – Part B: 1,20 kg. net

  • Total Set: 3 kg. net – Total Set : 3,90 kg. gross

*Barrels are available if requested.

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

APPEARANCE

Part A (Epoxy Resin): Liquid – Transparent

Part B (Epoxy Hardener): Liquid – Pale Yellow

PACKAGING

  • Part A: 12 kg. net – Part B: 8 kg. net

  • Total Set: 20 kg. net – Total Set : 22,55 kg. gross

  • Part A: 1,8 kg. net – Part B: 1,20 kg. net

  • Total Set: 3 kg. net – Total Set : 3,90 kg. gross

*Barrels are available if requested.

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

APPEARANCE

Part A (Epoxy Resin): Liquid – Transparent

Part B (Epoxy Hardener): Liquid – Pale Yellow

PACKAGING

  • Part A: 12 kg. net – Part B: 8 kg. net

  • Total Set: 20 kg. net – Total Set : 22,55 kg. gross

  • Part A: 1,8 kg. net – Part B: 1,20 kg. net

  • Total Set: 3 kg. net – Total Set : 3,90 kg. gross

*Barrels are available if requested.

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,08 kg/liter (± %3)

Viscosity

Mixed Resin: 900-1.300 mPa.s

Shore D Hardness

7 days: 75-85 (ASTM D2240-05)

Compressive Strength

28 days : > 95 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 30 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 20 mg (CS 10/1000/1000) (ASTM D4060-14)

Duration of Use After Mixing

45-60 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,08 kg/liter (± %3)

Viscosity

Mixed Resin: 900-1.300 mPa.s

Shore D Hardness

7 days: 75-85 (ASTM D2240-05)

Compressive Strength

28 days : > 95 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 30 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 20 mg (CS 10/1000/1000) (ASTM D4060-14)

Duration of Use After Mixing

45-60 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,08 kg/liter (± %3)

Viscosity

Mixed Resin: 900-1.300 mPa.s

Shore D Hardness

7 days: 75-85 (ASTM D2240-05)

Compressive Strength

28 days : > 95 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 30 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 20 mg (CS 10/1000/1000) (ASTM D4060-14)

Duration of Use After Mixing

45-60 minutes

Total Curing Time

7 days