TARDIGRADE

ERAP 950

SOLVENT FREE, TWO COMPONENT EPOXY RESIN ADHESIVE

Tardigrade ERAP 950 is a solvent free, two component epoxy resin adhesive mortar.

FIELDS OF APPLICATION

  • On concrete, natural stone, brick, wood, steel and metal surfaces
  • When the door and window frames are fixed
  • Gluing materials such as ceramics, tiles and granites to the surface
  • It is used as adhesive mortar

ADVANTAGES

  • Easy application
  • Can be used without primer
  • Solvent free
  • High bonding strength to concrete and steel
  • High loading capacity
  • High resistance against mechanical and chemicals
  • Durable against thermal shocks

TARDIGRADE

ERAP 950

SOLVENT FREE, TWO COMPONENT EPOXY RESIN ADHESIVE

Tardigrade ERAP 950 is a solvent free, two component epoxy resin adhesive mortar.

FIELDS OF APPLICATION

  • On concrete, natural stone, brick, wood, steel and metal surfaces
  • When the door and window frames are fixed
  • Gluing materials such as ceramics, tiles and granites to the surface
  • It is used as adhesive mortar

ADVANTAGES

  • Easy application
  • Can be used without primer
  • Solvent free
  • High bonding strength to concrete and steel
  • High loading capacity
  • High resistance against mechanical and chemicals
  • Durable against thermal shocks

TARDIGRADE

ERAP 950

SOLVENT FREE, TWO COMPONENT EPOXY RESIN ADHESIVE

Tardigrade ERAP 950 is a solvent free, two component epoxy resin adhesive mortar.

FIELDS OF APPLICATION

  • On concrete, natural stone, brick, wood, steel and metal surfaces
  • When the door and window frames are fixed
  • Gluing materials such as ceramics, tiles and granites to the surface
  • It is used as adhesive mortar

ADVANTAGES

  • Easy application
  • Can be used without primer
  • Solvent free
  • High bonding strength to concrete and steel
  • High loading capacity
  • High resistance against mechanical and chemicals
  • Durable against thermal shocks

APPEARANCE

Part A (Epoxy Resin) : Paste – Gray

Part B (Epoxy Hardener) : Paste – Cream

PACKAGING

  • Part A: 15 kg. net – Part B: 15 kg. net
  • Total Set: 30 kg. net – Total Set: 33 kg. gross
  • Part A: 3 kg. net – Part B: 3 kg. net
  • Total Set: 6 kg. net – Total Set: 7 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

APPEARANCE

Part A (Epoxy Resin) : Paste – Gray

Part B (Epoxy Hardener) : Paste – Cream

PACKAGING

  • Part A: 15 kg. net – Part B: 15 kg. net
  • Total Set: 30 kg. net – Total Set: 33 kg. gross
  • Part A: 3 kg. net – Part B: 3 kg. net
  • Total Set: 6 kg. net – Total Set: 7 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

APPEARANCE

Part A (Epoxy Resin) : Paste – Gray

Part B (Epoxy Hardener) : Paste – Cream

PACKAGING

  • Part A: 15 kg. net – Part B: 15 kg. net
  • Total Set: 30 kg. net – Total Set: 33 kg. gross
  • Part A: 3 kg. net – Part B: 3 kg. net
  • Total Set: 6 kg. net – Total Set: 7 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions.

CHEMICAL STRUCTURE

Part A: Epoxy Resin Part B: Epoxy Hardener

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,60 kg/litre (± %3)

Viscosity

Mixed Resin: 8.000 – 12.000 mPa.s

Shore D Hardness

7 days: 80 – 90 (ASTM D2240-05)

Compressive Strength

28 days: > 80 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 25 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 45 mg (CS 10/1000/1000)

(ASTM D4060-14)

Duration of Use After Mixing

50-70 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,60 kg/litre (± %3)

Viscosity

Mixed Resin: 8.000 – 12.000 mPa.s

Shore D Hardness

7 days: 80 – 90 (ASTM D2240-05)

Compressive Strength

28 days: > 80 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 25 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 45 mg (CS 10/1000/1000)

(ASTM D4060-14)

Duration of Use After Mixing

50-70 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,60 kg/litre (± %3)

Viscosity

Mixed Resin: 8.000 – 12.000 mPa.s

Shore D Hardness

7 days: 80 – 90 (ASTM D2240-05)

Compressive Strength

28 days: > 80 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 25 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 45 mg (CS 10/1000/1000)

(ASTM D4060-14)

Duration of Use After Mixing

50-70 minutes

Total Curing Time

7 days