TARDIGRADE

ERMT 900

THREE COMPONENT, SOLVENT FREE, EPOXY BASED REPAIR AND FILLING MORTAR

Tardigrade ERMT 900, is a three component, contain specific grade of aggregates, solvent free, epoxy based repair and filling mortar.

FIELDS OF APPLICATION

  • Industrial floorings
  • Joint repairs of highways
  • Concrete runways of airports
  • The maintenance and repair of marine structures
  • Bottom of crane rails
  • Bridge bearings and filling the empty space between the steel reinforcement of reinforced concrete columns
  • For the surface repairs before epoxy and polyurethane floor coating applications
  • Repair works of reinforced concrete elements

    It is used as a filling and repair mortar.

ADVANTAGES

  • Can be used without primer
  • High bonding strength to concrete and steel
  • High bonding strength
  • Solvent free
  • Does not shrink
  • High abrasion and impact resistance
  • High mechanical and chemical resistance

TARDIGRADE

ERMT 900

TWO COMPONENT, SOLVENT FREE, POLYURETHANE BASED, SELF LEVELING, ELASTIC COATING AND WATERPROOFING MATERIAL

Tardigrade ERMT 900, is a three component, contain specific grade of aggregates, solvent free, epoxy based repair and filling mortar.

FIELDS OF APPLICATION

  • Industrial floorings
  • Joint repairs of highways
  • Concrete runways of airports
  • The maintenance and repair of marine structures
  • Bottom of crane rails
  • Bridge bearings and filling the empty space between the steel reinforcement of reinforced concrete columns
  • For the surface repairs before epoxy and polyurethane floor coating applications
  • Repair works of reinforced concrete elements

    It is used as a filling and repair mortar.

ADVANTAGES

  • Can be used without primer
  • High bonding strength to concrete and steel
  • High bond strength
  • Solvent free
  • Does not shrink
  • High abrasion and impact resistance
  • High mechanical and chemical resistance

TARDIGRADE

ERMT 900

THREE COMPONENT, SOLVENT FREE, EPOXY BASED REPAIR AND FILLING MORTAR

Tardigrade ERMT 900, is a three component, contain specific grade of aggregates, solvent free, epoxy based repair and filling mortar.

FIELDS OF APPLICATION

  • Industrial floorings
  • Joint repairs of highways
  • Concrete runways of airports
  • The maintenance and repair of marine structures
  • Bottom of crane rails
  • Bridge bearings and filling the empty space between the steel reinforcement of reinforced concrete columns
  • For the surface repairs before epoxy and polyurethane floor coating applications
  • Repair works of reinforced concrete elements

    It is used as a filling and repair mortar.

ADVANTAGES

  • Can be used without primer
  • High bonding strength to concrete and steel
  • High bond strength
  • Solvent free
  • Does not shrink
  • High abrasion and impact resistance
  • High mechanical and chemical resistance

APPEARANCE

Part A (Epoxy Resin): Liquid – Transparent

Part B (Epoxy Hardener): Liquid – Pale Yellow

Part C (Aggregate) : Solid – Pale Yellow

PACKAGING

  • Part A: 2,65 kg. net – Part B: 1,35 kg. net – Part C: 16 kg. net
  • Total Set: 20 kg. net – Total Set: 22,75 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions..

CHEMICAL STRUCTURE

Part A : Epoxy Resin Part B: Epoxy Hardener Part C: Aggregate

APPEARANCE

Part A (Epoxy Resin): Liquid – Transparent

Part B (Epoxy Hardener): Liquid – Pale Yellow

Part C (Aggregate) : Solid – Pale Yellow

PACKAGING

  • Part A: 2,65 kg. net – Part B: 1,35 kg. net – Part C: 16 kg. net
  • Total Set: 20 kg. net – Total Set: 22,75 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions..

CHEMICAL STRUCTURE

Part A : Epoxy Resin Part B: Epoxy Hardener Part C: Aggregate

APPEARANCE

Part A (Epoxy Resin): Liquid – Transparent

Part B (Epoxy Hardener): Liquid – Pale Yellow

Part C (Aggregate) : Solid – Pale Yellow

PACKAGING

  • Part A: 2,65 kg. net – Part B: 1,35 kg. net – Part C: 16 kg. net
  • Total Set: 20 kg. net – Total Set: 22,75 kg. gross

STORAGE

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

SHELF LIFE

12 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one week as it is stored under appropriate storage conditions..

CHEMICAL STRUCTURE

Part A : Epoxy Resin Part B: Epoxy Hardener Part C: Aggregate

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,80 kg/litre (± %3)

Shore D Hardness

7 days: 80-90 (ASTM D2240-05)

Compressive Strength

28 days: > 80 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 30 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 45 mg (CS 10/1000/1000)

(ASTM D4060-14)

Duration of Use After Mixing

50-70 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,80 kg/litre (± %3)

Shore D Hardness

7 days: 80-90 (ASTM D2240-05)

Compressive Strength

28 days: > 80 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 30 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 45 mg (CS 10/1000/1000)

(ASTM D4060-14)

Duration of Use After Mixing

50-70 minutes

Total Curing Time

7 days

TECHNICAL SPECIFICATIONS

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density

Mixed Resin: 1,80 kg/litre (± %3)

Shore D Hardness

7 days: 80-90 (ASTM D2240-05)

Compressive Strength

28 days: > 80 N/mm² (ASTM D695-10)

Flexural Strength

7 days: > 30 N/mm² (ASTM D790)

Bond Strength

7 days : > 3 N/mm² (Concrete) (ASTM D7234)

Abrasion Strength

7 days: < 45 mg (CS 10/1000/1000)

(ASTM D4060-14)

Duration of Use After Mixing

50-70 minutes

Total Curing Time

7 days