TARDIGRADE

PUWP 320

TWO COMPONENT, SOLVENT FREE, SELF LEVELING, ELASTIC, POLYURETHANE WATERPROOFING MATERIAL

Tardigrade PUWP 320 is a polyurethane based, two component, low viscosity, solvent free, self leveling, cold applied, reaction cured, flexible and elastic waterproofing material.

In water tanks, pipes and channels
In the isolation of reservoirs
Under tile applications of wet floors such as bathrooms and kitchens
In the insulation of the places where odorless coating is required
Floor coverings on terraces and balconies
Insulation of indoor and outdoor swimming pools
In ornamental pool and underground water tank applications
Wet areas in the food, chemical and pharmaceutical industries
In production, storage and assembly areas
It is used as an insulation material in water insulation systems.

Low viscosity
Flexible and elastic
High bond strength
Solvent free
It is safe to use in drinking water storage and distribution channels.
Easy application
Can be used in constant contact with water
Maintains its elasticity at low temperatures
Hygienic and easy to clean
Provides complete water and moisture insulation

TARDIGRADE

PUWP 320

TWO COMPONENT, SOLVENT FREE, SELF LEVELING, ELASTIC, POLYURETHANE WATERPROOFING MATERIAL

Tardigrade PUWP 320 is a polyurethane based, two component, low viscosity, solvent free, self leveling, cold applied, reaction cured, flexible and elastic waterproofing material.

In water tanks, pipes and channels
In the isolation of reservoirs
Under tile applications of wet floors such as bathrooms and kitchens
In the insulation of the places where odorless coating is required
Floor coverings on terraces and balconies
Insulation of indoor and outdoor swimming pools
In ornamental pool and underground water tank applications
Wet areas in the food, chemical and pharmaceutical industries
In production, storage and assembly areas
It is used as an insulation material in water insulation systems.

Low viscosity
Flexible and elastic
High bond strength
Solvent free
It is safe to use in drinking water storage and distribution channels.
Easy application
Can be used in constant contact with water
Maintains its elasticity at low temperatures
Hygienic and easy to clean
Provides complete water and moisture insulation

TARDIGRADE

PUWP 320

TWO COMPONENT, SOLVENT FREE, SELF LEVELING, ELASTIC, POLYURETHANE WATERPROOFING MATERIAL

Tardigrade PUWP 320 is a polyurethane based, two component, low viscosity, solvent free, self leveling, cold applied, reaction cured, flexible and elastic waterproofing material.

In water tanks, pipes and channels
In the isolation of reservoirs
Under tile applications of wet floors such as bathrooms and kitchens
In the insulation of the places where odorless coating is required
Floor coverings on terraces and balconies
Insulation of indoor and outdoor swimming pools
In ornamental pool and underground water tank applications
Wet areas in the food, chemical and pharmaceutical industries
In production, storage and assembly areas
It is used as an insulation material in water insulation systems.

Low viscosity
Flexible and elastic
High bond strength
Solvent free
It is safe to use in drinking water storage and distribution channels.
Easy application
Can be used in constant contact with water
Maintains its elasticity at low temperatures
Hygienic and easy to clean
Provides complete water and moisture insulation

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating.

Part A: 25,50 kg. net – Part B: 4,50 kg. net
Total Set: 30 kg. net – Total Set: 32,55 kg. gross
Part A : 5,10 kg. net – Part B: 0,90 kg. net
Total Set: 6 kg. net – Total Set: 6,90 kg. gross

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

Shelf life is 9 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one day as it is stored under appropriate storage conditions.

Part A: Polyurethane Resin Part B: Polyurethane Hardener

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating.

Part A: 25,50 kg. net – Part B: 4,50 kg. net
Total Set: 30 kg. net – Total Set: 32,55 kg. gross
Part A : 5,10 kg. net – Part B: 0,90 kg. net
Total Set: 6 kg. net – Total Set: 6,90 kg. gross

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

Shelf life is 9 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one day as it is stored under appropriate storage conditions.

Part A: Polyurethane Resin Part B: Polyurethane Hardener

Mix (Part A + Part B) : Ral Colors

*Differences in color may occur under influence of direct sunlight. This does not affect the physical and chemical resistance of coating.

Part A: 25,50 kg. net – Part B: 4,50 kg. net
Total Set: 30 kg. net – Total Set: 32,55 kg. gross
Part A : 5,10 kg. net – Part B: 0,90 kg. net
Total Set: 6 kg. net – Total Set: 6,90 kg. gross

Store in original sealed containers in dry environment at temperatures between +10⁰C and +30⁰C. Do not put excessive loads on top of the products, which would damage the packaging.

Shelf life is 9 months from date of production if stored in original unopened containers. Once opened, product should be consumed within one day as it is stored under appropriate storage conditions.

Part A: Polyurethane Resin Part B: Polyurethane Hardener

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density	Mixed Resin: 1,45 kg/litre (± %3)
Viscosity	Mixed Resin: 2.000 – 3.000 mPa.s
Shore A Hardness	7 days: 80 – 90 (ASTM D2240-05)
Bond Strength	7 days : > 2,5 N/mm² (Beton) (ASTM D7234)
Solid Matter Ratio	~ 100%
Compressive Strength	28 days: > 10 N/mm² (ASTM D695-10)
Abrasion Strength	7 days: < 35 mg (CS 10/1000/1000) (ASTM D4060-14)
Elongation at Break	7 days: > % 150 (ASTM D638)
Duration of Use After Mixing	30 – 50 minutes
Total Curing Time	7 days

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density	Mixed Resin: 1,45 kg/litre (± %3)
Viscosity	Mixed Resin: 2.000 – 3.000 mPa.s
Shore A Hardness	7 days: 80 – 90 (ASTM D2240-05)
Bond Strength	7 days : > 2,5 N/mm² (Beton) (ASTM D7234)
Solid Matter Ratio	~ 100%
Compressive Strength	28 days: > 10 N/mm² (ASTM D695-10)
Abrasion Strength	7 days: < 35 mg (CS 10/1000/1000) (ASTM D4060-14)
Elongation at Break	7 days: > % 150 (ASTM D638)
Duration of Use After Mixing	30 – 50 minutes
Total Curing Time	7 days

All technical values were calculated based on +23⁰C and 50% relative humidity. Temperature and humidity changes would change technical values.

Density	Mixed Resin: 1,45 kg/litre (± %3)
Viscosity	Mixed Resin: 2.000 – 3.000 mPa.s
Shore A Hardness	7 days: 80 – 90 (ASTM D2240-05)
Bond Strength	7 days : > 2,5 N/mm² (Beton) (ASTM D7234)
Solid Matter Ratio	~ 100%
Compressive Strength	28 days: > 10 N/mm² (ASTM D695-10)
Abrasion Strength	7 days: < 35 mg (CS 10/1000/1000) (ASTM D4060-14)
Elongation at Break	7 days: > % 150 (ASTM D638)
Duration of Use After Mixing	30 – 50 minutes
Total Curing Time	7 days

CATALOGS

CORPORATE

DOCUMENTS

COMPOSITE RESINS

CONSTRUCTION CHEMICALS

NATURAL STONE RESINS

MARINE RESINS

CASTING RESINS

ARCHITECTURAL SOLUTIONS

TARDIGRADE

PUWP 320

TARDIGRADE

PUWP 320

TARDIGRADE

PUWP 320

TECHNICAL DOCUMENTS

CERTIFICATES

our catalogs